Fabrication of hierarchical PANI@W-type barium hexaferrite composites for highly efficient microwave absorption

Hexagonal barium ferries is a promising and efficient microwave (MW) absorbing material, but the low dielectric loss and poor conductivity have limited their extensive applications. In this work, a simple tactic of coating conductive polymer PANI on hexaferrite BaCo₂Fe₁₆O₂₇ is presented, wherein the dielectric properties are customized, and more significantly, the electromagnetic loss is greatly enhanced. As displayed from structural characterizations, PANI were coated equably on the surface of hexaferrite grains by an in-situ polymerization process. The outcomes exhibit the as-prepared PANI@hexaferrite composite has remarkable electromagnetic wave absorption capacity. When the thickness is 6.0 mm, the minimal RL of ?40.4 dB was achieved at 2.9 GHz. The effective absorption bandwidth (RL < ?20 dB) of 0.65 GHz, 0.53 GHz, 0.65 GHz, 0.52 GHz, 0.46 GHz and 0.39 GHz was achieved separately when the thickness ranges from 4 to 9 mm. The highly efficient MW absorbing performance of PANI@hexaferrite composite were the consequence of multiple loss mechanisms and perfect impedance matching. It is demonstrated that the PANI@hexaferrite composite with excellent MW absorption performance is expected to be potential MW absorbers for extensive applications.     

高碘酸盐的活化及降解水体有机污染物研究进展

根据高碘酸盐活化方式、活化机理和相关自由基种类等方面,叙述了国内外高碘酸盐高级氧化体系降解水体有机污染物方面的工作。基于氧化剂为高碘酸盐的高级氧化技术氧化能力强,能在较宽的pH范围内高效降解包括抗氧化能力极强的全氟辛酸(PFOA)在内的多种有机污染物,在水处理领域具有较好的应用潜力。依据目前的研究现状,结合实际需求,认为进行废水处理的小试或者中试、优化活化理论研究,以及明确各活性物质对有机物选择性降解的机理,是将来需要关注的问题以及研究方向。     

球形钛酸镍的制备及其电化学性能表征

钛酸镍(NiTiO3)是一种新型锂离子电池负极材料,采用溶胶.沉淀法可制备尺寸均匀、表面粗糙的球形NiTiO3颗粒.将制备的球形NiTiO3作为锂离子电池负极材料,具有良好的电化学性能,在0.1 C(50mA/g)时,其初始充电比容量约为375.6 mAh/g,库仑效率为52.1％;第二次充电比容量为331.3 mAh/g,库仑效率为90.9％;在1C时,其初始充电比容量为295.4mAh/g,经过前十次电池活化,循环20～100次的容量基本没有衰减,容量保持率高达99.7％.将球形NiTiO3与片状石墨复合,可提高首次库仑效率,改善循环性能,增加电子导电率,减小电池极化,有利于NiTiO3锂离子电池负极材料的工业应用.     

气藏型储气库注气期试井分析探讨

针对气藏型储气库注采井注采过程中储层物性参数影响因素不明确、注采能力不对称的问题。基于相国寺储气库井下连续油管试井测试结果,提出储气库注气期“温降效应”、“变表皮效应”的概念,分析了储气库注采过程中温降效应、变表皮效应以及储层应力敏感对注采的影响。通过气藏型储气库注气期试井分析技术,研究各因素在试井曲线上的响应特征以及对试井解释参数的影响。结果表明:①相对于采气期试井测试,注气期测试得到的储层物性参数具有同样的参考价值;②储气库温降效应对于试井解释结果的影响可忽略不计,而在不同注采运行周期内,变表皮效应以及应力敏感效应影响差异较大;③编制储气库注采运行方案时应充分考虑变表皮效应与应力敏感的影响,在不同注采运行周期内开展试井测试获取准确的储层参数值。研究成果为储气库试井测试与解释提供了重要的研究依据和理论指导。     

Influence of fermentation with different lactic acid bacteria and in vitro digestion on the change of phenolic compounds in fermented kiwifruit pulps

The present study aimed to evaluate the effect of fermentation and gastrointestinal digestion of three kinds of fermented kiwifruit pulps with different Lactobacillus (Lactobacillus plantarum, Lactobacillus acidophilus and Lactobacillus casei). The changes in bioactive substances (total phenolic acid, total flavonoid, vitamin C and the viable count), antioxidant capacity (DPPH, ABTS, hydroxyl radical and superoxide anion radical scavenging activity) and phenolic profiles (protocatechuic acid, protocatechualdehyde, chlorogenic acid, caffeic acid and p-coumaric acid) were detected. The result showed, compared to non-fermented kiwifruit pulp, fermentation with LP and LA had higher content of TPA, TF and V_C, as well as antioxidant capacity. Fermentation with LP and the content of protocatechualdehyde, p-coumaric acid and chlorogenic acid were increased. However, after digestion, LP showed more effect in maintaining the content of antioxidants, antioxidant capacity and the viable count rather than LA. During digestion, the content of protocatechualdehyde and p-coumaric acid was increased in fermented samples compared with non-fermented samples. Overall, compared with LA and LC, LP is more suitable for the fermentation of kiwifruit pulp.     

脉冲激光与电弧布置方式对铝合金焊接熔滴过渡与焊缝形貌的影响

以2219铝合金为基板，研究了不同脉冲激光-电弧布置方式下的熔滴过渡与焊缝形貌特征，分析了熔深增加的机理. 结果表明，当脉冲激光照射母材时，脉冲激光主要提供对母材的热输入，母材温度的增加有助于促进熔滴铺展，稳定熔滴过渡过程；当脉冲激光照射熔滴缩颈时，主要提供对熔滴的力输入，蒸发反力的作用下形成"一脉一滴"，显著提高熔滴过渡频率与熔滴飞行速度，增加了熔滴对熔池的冲击力，熔深增加；当脉冲激光交替的照射熔池和熔滴时，一方面能够对母材进行加热，有助于熔滴的铺展，另一方面能够提高熔滴过渡频率，提高焊缝的均匀性.     

超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性

针对100 mm超厚板TC4钛合金电子束焊接接头，采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性，分析接头的显微组织和断口形貌，对接头的腐蚀机制进行研究. 结果表明，室温条件下应变速率为ε=1×10-6 s-1时，母材在海水中未表现出应力腐蚀敏感性；焊缝上部、中部和下部具有轻微应力腐蚀敏感性. 焊缝在海水中发生阳极溶解，产生氢吸附，导致裂纹的萌生. 同时氢扩散诱导α'相界及α'相内发生位错塞积，进而使裂纹在更低的应力水平下发生扩展.     

Photoluminescence and thermal expansion of zirconium vanadate

The optical property and phase transition of ZrV₂O₇ were investigated by temperature-dependent X-ray diffraction, photoluminescence (PL), and Raman spectra. It was found that the material exhibited PL emission in the visible region. The temperature-dependent PL emission showed that the peak energy for emission (at red wavelength) presented a red shift from 10 to 80 K, and then a blue shift with the increase in temperature. The PL emission bands of ZrV₂O₇ shifted with change in temperature relating to its phase transition (80-100 K), which could be confirmed by temperature-dependent Raman spectra.